J Korean Assoc Maxillofac Plast Reconstr Surg.  2006 Sep;28(5):434-444.

Histomorphometric study of dental implants with double acid-etched and anodic oxidized surface in the rabbit tibia

Affiliations
  • 1Department of Oral and Maxillofacial Surgery, College of Medicine, Inha University, Korea. kik@inha.ac.kr

Abstract

This study was performed to evaluate the effects of three different implant surface treatments to the bone formation during osseous healing period under unloading conditions. Machined, double-acid etched and anodic oxidized implants were inserted into tibia of 3.0 - 3.5 kg NZ white male rabbits and 2 animals of each group were sacrificed at 2, 4 and 8 weeks. The specimens containing implant was dehydrated and embedded into hard methylmethacrylate plastic. After grinding to 50micrometer, the specimens were stained with Villanueva bone stain. From each specimen, histomorphometric evaluation and the bone implant contact rate were analysed with optical microscope. The results were as follows; 1. In the scanning electronic microscopic examination, machined surface implant had several shallow and paralleled scratches on plain surface, double acid-etched implant had lots of minute wrinkles, rough valley and also irregularly located craters that looked like waves, anodic oxidized surface implant had porosity that minute holes were wholly distributed on the surface. 2. After 2 weeks of implantation, the percentages of bone-to-implant contact in the machined implant, double acid-etched implant and anodic oxidized implant were 26.85%, 62.64% and 59.82%, after 4 weeks of implantation they were 64.29%, 77.85% and 75.23%, and after 8 weeks they were 82.66%, 85.34% and 86.39%. 3. After 2 weeks of implantation, the percentages of bone area between threads in the machined implant, double acid-etched implant and anodic oxidized implant were 21.55%, 42.81%, and 40.33%, after 4 weeks of implantation they were 49.32%, 62.60% and 75.56%, and after 8 weeks they were 71.62%, 87.73% and 83.94%. In summary, percentages of implant surface contacted to bone trabeculae and bone formation area inside threads in double acid-etched implants and anodic oxidized implants were greater than machined implants in early healing stage. These results suggest that double acid-etched and anodic oxidized surface implants could reduce the healing period for osseointegration and may enable to do early function.

Keyword

Implant; Tibia; Acid-etched; Anodic oxidized surface

MeSH Terms

Animals
Dental Implants*
Humans
Male
Methylmethacrylate
Osseointegration
Osteogenesis
Plastics
Porosity
Rabbits
Tibia*
Dental Implants
Methylmethacrylate
Plastics
Full Text Links
  • JKAMPRS
Actions
Cited
CITED
export Copy
Close
Share
  • Twitter
  • Facebook
Similar articles
Copyright © 2024 by Korean Association of Medical Journal Editors. All rights reserved.     E-mail: koreamed@kamje.or.kr