J Adv Prosthodont.  2020 Jun;12(3):114-123. 10.4047/jap.2020.12.3.114.

Evaluation of corrosion resistance of Co-Cr alloys fabricated with different metal laser sintering systems

• Tuna SH
• Karaca E
• Aslan
• Pekkan G
• Pekmez N

• KMID: 2504119
• DOI: http://doi.org/10.4047/jap.2020.12.3.114

Abstract

PURPOSE
. The aim of this study was to evaluate the corrosion resistance of the specimens produced by five different commercial metal laser sintering (MLS) systems with their recommended Co-Cr alloy powders.
MATERIALS AND METHODS
. The MLS machines and the alloy powders used were, ProX 100-ST2724G (St-Pro), Mysint 100-EOS SP2 (SP2-Mys), EOSINT 270-EOS SP2 (SP2-EOS), SLM 100-Starbond CoS (SB-SLM), and MLab Cusing-Remanium^® Star (RS-MLab), respectively. Eight specimens from each group were prepared. Open circuit potential (E_ocp) and electrochemical impedance spectroscopy (EIS) measurements of polished surfaces of the specimens were conducted in a three-electrode cell using a potentiostat-galvanostat in Fusayama-Meyer artificial saliva (AS). Specimens from each group were immersed in AS and de-ionized water for seven days. E_ocp, charge transfer resistance (R_ct) values, and released ions (μg/cm² × 7d) in different solutions were determined. The specimen surfaces were observed with SEM/EDS. Results were analyzed statistically.
RESULTS
. E_ocp values have shifted to potentials that are more positive over time. Steady-state E_ocp values were from high to low as follows, SB-SLM, SP2-Mys, SP2-EOS, RS-MLab, and ST-Pro, respectively. After 60 mins, RS-MLab specimens had the highest R_ct value, followed by SP2-Mys, SB-SLM, SP2-EOS, and ST-Pro. In all groups, ion release was higher in AS than that in de-ionized water.
CONCLUSION
. There were small differences among the corrosion resistances of the Co-Cr alloy specimens produced with MLS systems; meanwhile, the corrosion resistances were quite high for all specimens.

Keyword

Co-Cr alloy; Corrosion; Metal laser sintering; Powder