J Korean Acad Prosthodont.  1997 Mar;35(1):78-94.

A STDUY ON THE SURFACE MORPHOLOGY AND BOND STRENGTH OF DENTURE BASE RESIN TO COBALT-CHROMIUM ALLOY AFTER VARYING MODES OF SURFACE TREATMENT

• Vang MS
• Park YJ

Abstract

The purpose of this experiment was to determine the effects of various treatments on denture base resin to metal bond for cobalt-chromium alloy. The metal surface was treated as follows. Group 1 : Sandblasted with 50microneter aluminum oxide. Group 2 : Sandblasted with 250microneter aluminum oxide. Group 3 : Sandblasted with 250microneter aluminum oxide and followed by silicoating. Group 4 : Electrochemically etched. Group 5 : treated with oxidizing solution. Group 6 : Beaded with 200microneter retention structure and followed by silicoating. All specimens were applied with 4-META resin and were thermocycled 1000 times at temperature of 5degrees C to 55degrees C. The effects of various surface treatments on the bond strength between 4-META resin and metal interface were measured by using the universal testing machine. All specimens were observed with SEM. The results were as follows 1. The bond strength of 4-META resin were significantly higher to Co-Cr alloy. 2. The bond strength decreased in the following orders : group 6, group 3, groups 1 and 2, group 4, group 5 and there was no statistically significant difference in bond strength among groups 1 and 2. (p>0.05) 3. The bond strength of cobalt-chromium alloy to 4-META resin were not significantly different. (p>0.05) 4. The treated surface of groups 1, 2 and 3 has more fine undercut than that of groups 4 and 5 with SEM. 5. Stable adhesion can be achieved when mechanically roughened metal surface by sandblasting than treating in an electrochemical etching and an oxidizing solution with potassium manganate.

MeSH Terms

Alloys*
Aluminum Oxide
Denture Bases*
Dentures*
Potassium
Alloys
Aluminum Oxide
Potassium