J Korean Acad Prosthodont.  1999 Dec;37(6):809-819.

THE STUDY ON THE PHYSICAL PROPERTY OF THE PERMANENT SOFT DENTURE LINERS

• Kim YM
• Bae JS

Abstract

This study was performed to evaluate the tensile bond strength and modulus of elasticity of three permanent soft denture liners (Molloplast B , Ufi Gel C , Tokuyama ) before and after thermocycling. And their water sorption were also evaluated. Each soft denture liner was bonded to PMMA denture base resin blocks and the tensile bond strength and modulus of elasticity were measured by using universal testing machine. For the water sorption, weight measured after immersion of soft denture liners in 37+/-1degrees C water bath for 4 weeks. The results were as follows : 1. Molloplast B had the highest tensile bond strength, while Tokuyama had the lowest tensile bond strength, There was no significant difference between Tokuyama and Molloplast B in the both nonthermocycling and thermocycling. There was significant difference in tensile strength of Tokuyama before and after thermocycling(p<0.05). 2. For the modulus of elasticity, there was no significant difference between Ufi Gel C and Tokuyama in the both nonthermocycling and thermocycling. There was significant difference in modulus of elasticity of Tokuyama before and after thermocycling(p<0.05). 3. The failure modes of Molloplast B and Ufi Gel C were nainley adhesive type and that of Tokuyama was mainly mixed type in case of nonthermocycling and cohesive type after thermocycling. 4. The water sorption of each soft liners was within+/-2% in times (p<0.05) but, there was no significant difference among the soft liners in times.

MeSH Terms

Adhesives
Baths
Denture Bases
Denture Liners*
Dentures*
Elastic Modulus
Immersion
Polymethyl Methacrylate
Tensile Strength
Water
Adhesives
Polymethyl Methacrylate
Water