J Korean Acad Prosthodont.  2003 Aug;41(4):476-492.

Effect of hema and tegdma on the properties of experimental composite resins

• Han MH

Abstract

PURPOSE
The purpose of this study was to compare HEMA and TEGDMA as diluents for the composite resin. MATERIAL AND METHODS: Eight kinds of experimental light curable composite resins were prepared and used. Concentrations of monomer and filler were same for all experimental composites, except, the diluent's ratios to the monomer. The ratio of diluents to Bis-GMA were 15%, 20%, 25%, and 30%, and two kinds of diluents were used, so total experimental groups were eight including one control group of 25% TEGDMA. RESULTS: Depth of cure, flexural strength, shear bond strength to bovine enamel, shear bond strength to bovine dentin, water absorption and solubility of composites in water were measured. Sample size for each groups were 10. Arithmetic means were used as each groups representative values, and regression test for two diluents and four concentrations, Duncan's multiple range test, and Two-way ANOVA test were done for kinds of diluents and its concentrations at level of 0.05. CONCLUSION: Following results were obtained; 1. There were not significant differences in effects of HEMA and TEGDMA to depth of cure, flexural strength of composites and shear bond strength to bovine enamel (p>0.05). 2. Increase of the concentrations of the diluents made the depth of cure (p<0.001) and flexural strength (p<0.05) a little higher. 3. Shear bond strength to dentin was higher on HEMA containing composites than TEGDMA containing composites (p<0.001). 4. Water absorption was higher on HEMA containing composites than TEGDMA containing composites (p<0.01).

Keyword

HEMA; TEGDMA; depth of cure; flexural strength; Shear bond strength