A STUDY ON THE FLEXURAL STRENGH OF HEAT-PRESSED CERAMICS ACCORDING TO SPRUE DESIGNS

• Oh SC
• Dong JK

Abstract

A heat-pressed technique(IPS-Empress, Ivoclar) has been described to construct single unit crown, inlay/onlay and veneers using a partially pre-cerammed and pre-colored glass-leucite ingot that has the greateast strength by the combination of heat-pressed procedure through the small-diameter sprue and heat treatment procedure. The purpose of this study was to evaluate the flexure strength of a heat-pressed ceramic material(IPS-Empress) without simulated firing treatments according to pontic designs. Two groups of 9 disks(1.4mm thick, 14mm in diameter) each using two types of sprues with different diameters(phi2.8, phi1.8) and numbers were prepared. The specimens were mounted in the testing jig. The flexural strengths were determined, by means of the bi-axial bending test, by loading the center of disk to failure using a universal testing machine(Zwick 145141, Zwick, Germany) at a cross-head speed of 1.0 mm/min. The means flexural strength value of one group using a sprue with phi2.8 was 140.4+/-8.0 Mpa. That of the other group using two sprues with phi1.8 was 151.8+/-10.3 Mpa. After analysis, results showed that there was a statistical difference between groups(t=2.33m p<0.05). No clnical implications were drawn from these data because of absence of simulated firing treatment.

MeSH Terms

Celiac Disease*
Ceramics*
Crowns
Denture, Partial, Fixed
Fires
Hot Temperature
Ceramics