J Korean Acad Periodontol.  2007 Jun;37(2):251-263. 10.5051/jkape.2007.37.2.251.

The effects of tetracycline-HCl on SLA implant surface structure

Affiliations
  • 1Department of Periodontology and Institute of Oral Biology, School of Dentistry, Kyung Hee University, Korea. kyhyuk@khu.ac.kr

Abstract

The present study was performed to evaluate the effects of Tetracycline-HCl on the microstructure change of SLA implant surface according to application time. In the Tetracycline-HCl group, 6 implants were rubbed with sponges soaked 50mg/ml Tetracycline-HCl solution for 0.5min., 1min., 1.5min., 2min., 2.5min. and 3min. In the saline group, another 6 implants conditioned with sponges soaked saline using same methods. One implant wasn't conditioned anything. Then, the changes of surface roughness values were evaluated by optical interferometer & specimens were processed for scanning electron microscopic observation. The results of this study were as follows: 1. In both Tetracycline-HCl group & saline group, there are no significant differences between surface roughness values before & after surface detoxification. And in scanning electron microscopic observation, there are slightl9y changes of implant surface structures but this changes were not significant by comparison with no treatment implant surface. 2. In the changes of surface roughness values & the scanning electron microscopic observation, there were no significant differences between saline & Tetracycline-HCl groups. In conclusion, the detoxification with 50mg/ml Tetracycline-HCl within 3 minutes can be applied for treatment of peri-implantitis in SLA surface implants, without surface microstructure changes.

Keyword

Tetracycline-HCl; SLA implant surface; Peri-implantitis

MeSH Terms

Peri-Implantitis
Porifera
Full Text Links
  • JKAPE
Actions
Cited
CITED
export Copy
Close
Share
  • Twitter
  • Facebook
Similar articles
Copyright © 2024 by Korean Association of Medical Journal Editors. All rights reserved.     E-mail: koreamed@kamje.or.kr