Attachment and proliferation of human gingival fibroblasts on the implant abutment materials
- Affiliations
-
- 1Department of Prosthodontics, Graduate School, Chonnam National University, Korea.
Abstract
- PURPOSE
The biocompatibility and bio-adhesive property of a dental implant abutment are important for proper soft tissue healing and maintenance of osseointegration of implant. However, studies of soft tissue healing and mucosal attachment of various materials of implant abutment other than titanium are still needed. In this study, cell attachment, proliferation, cytotoxicity of human gingival fibroblast for ceramic, gold alloy, Ni-Cr alloy and, commercially available pure titanium as a control were evaluated, using MTS and scanning electron microscopy.
MATERIALS AND METHODS
Specimen was designed to disc, 4mm diameter and 1mm thickness, made of ceramic, gold alloy, Ni-Cr alloy and commercially available pure titanium. Primary culture of human gingival fibroblasts were grown in Dulbecco's modified Eagle's medium with 10% fetal bovine serum and 1% antibiotics. Cells were inoculated in the multiwell plates placed the specimen disc. Cell Titer 96 AQucous One Solution Cell Proliferation Assay were done after 1hour, 3hours, 24hours, 3days, 5days of incubation. The discs were processed for scanning electron micrography to evaluate cell attachment and morphologic change.
RESULTS
The results were obtained as follows. 1. The ceramic showed high cell attachment and proliferation and low cytotoxicity, which is as much bioadhesive and biocompatible as titanium. 2. The gold alloy represented limited proliferation of human gingival fibroblast and the highest cytotoxicity among tested materials (p<0.05). 3. The Ni-Cr alloy limited the proliferaion of the human gingival fibroblast compared to titanium(p<0.05), but cytotoxicity on the bottom of well was not so considerable, compared to titanium. 4. On the scanning electron micrographs, the ceramic showed good attachment and proliferation of human gingival fibroblast, which was similar to titanium. But gold alloy and Ni-Cr alloy showed the shrinkage of gingival fibroblast both after 24 hours and 3 days. On 5th day, small amount of the human gingival fibroblast proliferation was observed on the Ni-Cr alloy, while the shrinkage of gingival fibroblast was still observed on the gold alloy.
CONCLUSIONS
These results suggest that the ceramic abutment is as biocompatible as titanium to make proper mucosal seal. The gold alloy has a high cytotoxicity to limit proliferation of gingival fibroblast, which suggest limited use on the anterior tooth where soft tissue healing is recommeded.